Polyken 2036 is a primary anti-corrosion joint wrap tape designed for use in field coating applications. 2036 joint wrap tape provides superior bond strength to primed steel, has a continuous operating service temperature up to 200°F, and has excellent conformability when applied to pipe.

Polyken 2036 joint wrap tape consists of a special polyethylene with very high resistance to environmental stress cracking combined with an engineered butyl alloy based adhesive, which cures when the coated pipeline begins operating at its elevated temperature. This curing gives superior resistance to shear and soil stress. It has proven in-ground success against chemical and electrolytic corrosion due to the combined effects of the polyethylene and butyl adhesive components.

Polyken 2036 is a high temperature coating which will have satisfactory performance up to 200°F continuous operating temperature. This product should be used with a special high shear Polyken primer, such as 2019 or 2027.

Product Features & Benefits
Proven Performance: Polyken 2036 is part of the total Polyken product coating system, which is used on a world-wide basis under all types of pipeline construction specifications.	Integral Bond: Polyken 2036 will bond to the specially primed steel surface providing for long-term, high quality, anti-corrosion performance. Ease of Application: Can be applied using conventional application equipment.

Product Properties
Backing Polyethylene, stress-crack resistant with high temperature stabilizers. Color: Black.
Adhesive Engineered butyl alloy with synthetic resins and additives for curing when on primed pipe at elevated temperature.
Physical Properties	English	Metric
Total thickness Backing thickness Adhesive thickness Tensile strength Elongation Adhesion to primed steel plate	25 mil 13 mil 12 mil 40 lb/in 400% 250 oz/in	0.64 mm 0.33 mm 0.31 mm 70 N / 10 mm 400% 20 N / 10 mm
Electrical & Moisture	English	Metric
Dielectric strength Insulation resistance Volume resistivity Specific resistance Water vapor transmission rate	22 kV > 10¹² Ohm in > 10¹⁵ Ohm in 7 x 10¹⁶ Ohm ft²< 0.04 gm/100 in²/24 hr	22 kV > 10¹² Ohm cm > 10¹⁵ Ohm cm 6 x 10⁹⁶ ohm m²< 0.6 gm/m²/24 hr
Note: Dielectric strength is not intended as a suggested holiday voltage. Refer to NACE Standard RP-02-74 for recommended holiday voltage.
Temperature Range	English	Metric
Normal application Norma continuous service Interim short interval operating temperature	-30°F to 160°F -30°F to 200°F -30°F to 220°F	-34°C to 71°C -34°C to 93°C -34°C to 104°C
Test Methods
1. ASTM D 100 2. ASTM D 149 3. ASTM D 257 4. ASTM F 1249 (100°F, 100% R.H.) 5. DIN 30672

Updates at Farwest Corrosion

Polyken # 2036 High Temperature Anti-Corrosion Joint Wrap Coating

A primary anti-corrosion joint wrap designed for superior bond strength to primed steel and continuous operating service temperature up to 200°F.