One-coat, stand-alone protection that exceeds all performance criteria for corrosion prevention of above and below ground metal surfaces.

Available in:

1-Pint Kits, 4 per case

1-Quart Kits, 2 per case

1-Gallon Kits, 2 per case



Tapecoat TC 7030 High-Build, High-Temperature Epoxy is a one-coat, stand-alone protection that exceeds all performance criteria for prevention of corrosion of above and below ground metal surfaces. This tough coating can be used for any general application including high temperature pipelines with a maximum constant operating temperature of up to 250°F (121°C).

TC 7030 is an environment-friendly two-component, 100% solids material that provides up to 30 mils of high-build thickness for tough abrasion resistance-to-backfill and soil stress damage. This surface-tolerant epoxy provides exceptional corrosion prevention for reconditioning pipelines, protecting joints, patching pipeline coatings, and covering irregular fittings and metal surfaces.



Red. Additional colors available upon request.

Pot Life

15 to 20 min at 70°F (121°C) and 50% R.H.

Max Constant Operating Temp

250°F (121°C)



Mixing Ratio

3.6:1 by volume


No Red Label required


Surface must be clean and dry. Commercial blast to SSPC-SP6. Remove oil and grease with suitable solvent. Salt and other contaminants may be removed by high pressure fresh water cleaning. Pour entire contents of Part B Curing Agent (small container) into Part A Resin (large container), and mix thoroughly for approximately 3 to 5 minutes. Do not alter the amounts of A and B in the mixture. Apply epoxy by brush, pad, roller or spray.

Primer should be dry to touch before applying Tapecoat hot applied tapes or sleeves. As a stand alone coating, TC 7030 Epoxy provides superior corrosion protection above and below ground.

Specially selected Tapecoat reinforcing scrim can be applied over wet epoxy. After scrim has been applied, apply a second coat of TC 7030 Epoxy.

Application Parameters


Use only when the surface to be coated is above 40°F (4°C) and the relative humidity (R.H.) is less than 90%.

Application temperature

40°F-250°F (4°C-121°C). Surface temperature must be 5°F
(3°C) above the dew point to avoid condensation.

Cure time

60 to 90 minutes at 70°-80°F (21°-27°C) and 50% R.H. Cure time can be accelerated by preheating the metal surface to 100°F-200°F (38°-93°C).

Recommended coverage

Single-coat, stand-alone coating: 30 mils (0.76mm) thickness, with a coverage of 53 sq. ft. per mixed gallon (1.23 m2/liter)